An Experimental Hot Corrosion Study of HVOF Sprayed NiCr50Al and WC-1 - Malhi, Gurmail Singh;Garg, Sourav
26,99 €
inkl. MwSt.
Versandkostenfrei*
Versandfertig in 6-10 Tagen
payback
13 °P sammeln
  • Broschiertes Buch

This is an experimental study conducted on bare and coated T91 boiler tube steel in the salty environment. The comparative resistance of coating with bare steel had been analyzed after identification of crucial hot corrosion problem from past literature reviews. Two coatings NiCr50Al and WC-17Co had been deposited on steel samples by HVOF thermal spray. The outcomes of study showed that coated surfaces showed greater resistance to the hot corrosion.

Andere Kunden interessierten sich auch für
Produktbeschreibung
This is an experimental study conducted on bare and coated T91 boiler tube steel in the salty environment. The comparative resistance of coating with bare steel had been analyzed after identification of crucial hot corrosion problem from past literature reviews. Two coatings NiCr50Al and WC-17Co had been deposited on steel samples by HVOF thermal spray. The outcomes of study showed that coated surfaces showed greater resistance to the hot corrosion.
Autorenporträt
Gurmail Singh Malhi received Ph.D. from the Department of Mechanical Engineering, IKG PTU. He has total 13 years of experience  of teaching in two universities. Now ,he is working as assistant professor  in department of aerospace at Chandigarh University. Dr. Malhi has published 20 papers in referred  international journals.