Characteristics and Thermal Behavior of Sputtered Titanium Thin Films on Various Substrates
-
- Englisch ausgewählt
59,99 €
UVP
71,90 €
inkl. gesetzl. MwSt.,
Lieferung nach Hause
Beschreibung
Produktdetails
Einband
Taschenbuch
Erscheinungsdatum
09.07.2019
Verlag
LAP LAMBERT Academic PublishingSeitenzahl
200
Maße (L/B/H)
22/15/1,3 cm
Gewicht
316 g
Sprache
Englisch
ISBN
978-3-659-97348-2
Titanium films are growing in popularity, and are soon expected to replace copper for metallization purposes. However, the thermal stress behavior of titanium films had not been extensively studied, and therefore not clearly understood. Thus, the main goal of this work was to develop a systematic process to analyze and model the d¿/dT evolution between 20ºC and 300ºC, in sputtered, titanium thin films. A biaxial stress state has been legitimately assumed. In the laboratory, titanium films, with a nominal thickness of 200 nm, were deposited on five different kinds of unheated substrates, by RF magnetron sputtering. These substrates included titanium plate, soda-lime glass and three kinds of p-type silicon wafers, having crystallographic orientations of (100), (110) and (111). X-ray diffraction was used to characterize the crystallographic evolution with respect to temperature. By utilizing a heating chamber and special tooling, the lattice spacings were measured in-situ, and the thermal stress behaviors were estimated with either the sin2¿ method or the d-spacing method.
Noch keine Bewertungen vorhanden
Verfassen Sie die erste Bewertung zu diesem Artikel
Helfen Sie anderen Kundinnen und Kunden durch Ihre Meinung.
Kurze Frage zu unserer Seite
Vielen Dank für dein Feedback
Wir nutzen dein Feedback, um unsere Produktseiten zu verbessern. Bitte habe Verständnis, dass wir dir keine Rückmeldung geben können. Falls du Kontakt mit uns aufnehmen möchtest, kannst du dich aber gerne an unseren Kund*innenservice wenden.
zum Kundenservice