Creep Behavior of an Oxide/Oxide Composite with Monazite Coating at Elevated Temperatures
Versandkostenfrei!
Versandfertig in über 4 Wochen
55,99 €
inkl. MwSt.
PAYBACK Punkte
28 °P sammeln!
This study focuses on experimental investigation of stress-rupture behavior (creep response) of an oxide/oxide composite in a cross-ply (0/90) lay-up at elevated temperature. The test material, Nextel 610/monazite/alumina composite, employs monazite, an oxidation-resistant interfacial coating designed to improve performance at elevated temperatures. The experimental program included monotonic tensile tests to failure and creep-rupture tests at elevated temperatures. Tensile tests served to establish an ultimate tensile strength (UTS) for the material. The ensuing creep-rupture tests involved s...
This study focuses on experimental investigation of stress-rupture behavior (creep response) of an oxide/oxide composite in a cross-ply (0/90) lay-up at elevated temperature. The test material, Nextel 610/monazite/alumina composite, employs monazite, an oxidation-resistant interfacial coating designed to improve performance at elevated temperatures. The experimental program included monotonic tensile tests to failure and creep-rupture tests at elevated temperatures. Tensile tests served to establish an ultimate tensile strength (UTS) for the material. The ensuing creep-rupture tests involved stress levels at varying percentages of the UTS. Stress-rupture curves at 900 and 1100oC were established. A family of creep curves for various constant stress levels at 900 and 1100oC was produced. Composite microstructure, as well as damage and failure mechanisms were also investigated.
Andere Kunden interessierten sich für